Enhanced creep resistance of Ti30Al25Zr25Nb20 high-entropy

已有 405 次阅读 2021-7-6 08:42 |个人分类:材料科学|系统分类:论文交流

Enhanced creep resistance of Ti30Al25Zr25Nb20 high-entropy alloy at room temperature

D.Wanga J.Tanab C.J.Lia X.M.Qinb S.F.Guoc

  • Faculty of Materials Science and Engineering, Kunming University of Science and Technology, 650093 Kunming, China

  • College of Materials Science and Engineering, Chongqing University, 400044 Chongqing, China

  • Faculty of Materials and Energy, Southwest University, 400715 Chongqing, China


Abstract

Several previous studies have shown that the dissolution of Al in a solid solution single phase BCC is high unfavorable in TiZrNb system. In this work, a novel Ti30Al25Zr25Nb20 high-entropy alloy (HEA) with a single body-centered cubic (bcc) structure was developed. The Young's modulus and nano-hardness of this HEA measured by continuous stiffness measurement (CSM) technique were 158.2 ± 5.2 GPa and 8.9 ± 0.2 GPa, respectively. The creep behaviors of this HEA at a constant temperature of 20 °C under different loading rates and peak loads were studied by nano-indentation technique. The result indicated that with the increase of loading rates and peak loads, the creep displacement increased, but the creep strain rate sensitive index first decreased and then increased, and the physical mechanisms are interrupted by introducing dislocation activation volume. The reason might attribute to the hysteresis diffusion effect. Compared with other metallic structural materials, Ti30Al25Zr25Nb20 HEA possesses a relatively high dislocation activation volume and low creep strain rate sensitive index value, indicating a significantly high creep resistance.



https://doi.org/10.1016/j.jallcom.2021.161038





https://wap.sciencenet.cn/blog-4773-1294247.html

上一篇:发明高温钼基块体非晶合金
下一篇:Ternary Fe–W–B bulk metallic glasses

0

该博文允许注册用户评论 请点击登录 评论 (0 个评论)

数据加载中...

Archiver|手机版|科学网 ( 京ICP备07017567号-12 )

GMT+8, 2021-9-28 15:10

Powered by ScienceNet.cn

Copyright © 2007- 中国科学报社

返回顶部