Enhanced mechanical properties and degradation rate

已有 2312 次阅读 2020-3-21 17:52 |个人分类:材料科学|系统分类:论文交流

Enhanced mechanical properties and degradation rate of Mg–Ni–Y alloy by introducing LPSO phase for degradable fracturing ball applications


Jingfeng Wanga  Shiqing Gaoa  Xiuying Liua  Xing Penga  Kui Wanga  Shijie Liua  Weiyan Jianga  Shengfeng Guob  Fushen Pana


Abstract

In this work, as-cast Mg–Ni–Y alloys were proposed to develop a feasible material for fracturing balls, and their mechanical performance and corrosion behavior were systematically investigated. Long period stacking order (LPSO) phase was firstly introduced to improve both the mechanical properties and degradation rate of magnesium alloys. With the increase of LPSO phase, the compressive strength was improved significantly, while the elongation of the alloys decreased owing to the relatively brittle nature of LPSO phase. Due to the higher corrosion potential of LPSO phase, the LPSO phase can accelerate the corrosion process by providing more micro-couples. However, the LPSO phase would serve as the corrosion barrier between the corrosion medium and the matrix when the contents of LPSO phase are too high in Mg92.5Ni3Y4.5 and Mg87.5Ni5Y7.5 alloys. As-cast Mg97.5Ni1Y1.5 alloy with satisfactory mechanical properties and rapid degradation rate was successfully developed, exhibiting a high degradation rate of 6675 mm/a (93 °C) in 3 wt.% KCl solution and a favorable ultimate compressive strength of 410 MPa. The degradation rate of Mg97.5Ni1Y1.5 alloy is 2–5 times of the current commercial magnesium alloy fracturing materials.


https://www.sciencedirect.com/science/article/pii/S2213956720300116





https://wap.sciencenet.cn/blog-4773-1224624.html

上一篇:Fabrication of a Zr-based bulk metallic glass surface
下一篇:中国铝产业的发展现状及展望
收藏 IP: 111.60.233.*| 热度|

0

该博文允许注册用户评论 请点击登录 评论 (0 个评论)

数据加载中...
扫一扫,分享此博文

Archiver|手机版|科学网 ( 京ICP备07017567号-12 )

GMT+8, 2024-12-14 18:27

Powered by ScienceNet.cn

Copyright © 2007- 中国科学报社

返回顶部