壳层中高Yb含量对核壳结构纳米晶上转换性能的影响
陈大钦 2014-9-10 10:30
After coating NaYbF 4 shell on the 20Yb/2Er: NaGdF 4 core nanocrystals, upconversion emission intensity decreased. Through acore@shell@shell sandwich like structure, we find that high Yb 3+ concentration in the shell has mainly two adverse impacts: it promotes not only the deleterious back-energy- ...
个人分类: 科学研究|3725 次阅读|没有评论
近红外长余辉发光透明玻璃陶瓷
陈大钦 2014-9-10 10:16
Cr 3+ doped transparent glassceramics of SiO 2 -Ga 2 O 3 -Li 2 O werefabricated by melt-quenching and subsequent crystallization. X-ray diffractionand transmission electron microscopy analyses evidenced that cubic LiGa 5 O 8 nanocrystals were homogeneously precipitated among the silicate ...
个人分类: 科学研究|4236 次阅读|没有评论
近红外长余辉-近红外上转换双功能荧光体:Cr/Yb/Tm:Ca3Ga2Ge3O12
陈大钦 2014-9-10 10:05
Currently, upconversion nanocrystals and long-lasting phosphorescent particles have attracted extensive research interests for their possible applications as bio-imaging probes. However, there are few reports concerning the achievement of both upconversion luminescence of lanthanide ions an ...
个人分类: 科学研究|4211 次阅读|没有评论
新型近红外长余辉荧光体:Cr3+: SrGa12O19
陈大钦 2014-9-10 09:50
A NIR long persistent Cr 3+ : SrGa 12 O 19 phosphor with persistent time lasting formore than 2 h has been successfully fabricated.The doped Cr 3+ ions prefer to occupy the octahedral sites of Ga 3+ with the intermediate crystal field strength. The NIR LPP can be effectively realized by UV ...
个人分类: 科学研究|4102 次阅读|没有评论
量子剪裁下转换发光活性核-活性壳纳米晶
陈大钦 2014-9-10 09:35
Monodisperse Pr 3+ /Yb 3+ :NaGdF 4 @NaYF 4 active-core/inert-shell nanoparticles, whichexhibit efficient near-infrared quantum cutting luminescence, are successfullyprepared. In order to relieve the adverse effect caused by concentration quenching in the core, the extra Yb 3+ ions are ...
个人分类: 科学研究|4062 次阅读|没有评论
发光核壳纳米晶:核尺寸对壳层生长的影响
陈大钦 2014-9-10 09:13
The purpose of the present work is to demonstrate that the hexagonal Yb/Er:NaGdF4core size has a great impact on the completeness of the NaYF4 shell coveringthe core. With the increase of core size, the morphology of core–shell nanocrystals evolves from nanosphere to hexagonal nanoprism and fi ...
个人分类: 科学研究|3265 次阅读|没有评论
高功率白光LED用新型光转化材料:透明Ce3+: YAG微晶玻璃
热度 5 陈大钦 2014-1-14 22:53
目前国际上主流的白光 LED 器件是将 Ce : YAG 荧光粉分散在环氧树脂或硅胶中然后再涂敷在蓝光芯片上所构成。环氧树脂或硅胶在大功率芯片产生的高温环境下,容易发生老化,颜色变黄,使得 LED 产生色偏和光衰,缩短了其使用寿命。因此,研发光学性能优越、物化稳定性高的新型荧光材料来代替 Ce : YAG/ 有机基质荧光体 ...
个人分类: 科学研究|6644 次阅读|5 个评论 热度 5
离子掺杂调控纳米晶尺度及核壳结构完整性获得进展
热度 1 陈大钦 2013-10-12 10:47
最近, 我们发现 在氟化钆钠( NaGdF 4 )纳米晶中掺杂 Ca 2+ 离子(用来替代 Gd 3+ )后,可诱导纳米晶生长受扩散过程控制,有效地实现纳米晶尺度及均匀性的调控 ;同时,以 Ca 2+ 掺杂 Yb/Er:NaGdF 4 纳米晶作为核,可以实现 NaYF 4 壳层在其上的完整生长 ,获得高效上 ...
个人分类: 科学研究|4306 次阅读|2 个评论 热度 1
“离子掺杂:一种可控合成镧系纳米晶新技术”综述论文在线发表
热度 3 陈大钦 2013-5-7 08:31
“离子掺杂:一种可控合成镧系纳米晶新技术”综述论文在线发表(Nanoscale, 2013, DOI: 10.1039/C3NR00368J ) 全文链接:http://pubs.rsc.org/en/content/articlelanding/2013/nr/c3nr00368j
3369 次阅读|4 个评论 热度 3
无序固溶体纳米晶中的反常尺寸依赖上转换发光
热度 1 陈大钦 2013-2-6 10:20
无序固溶体纳米晶中的反常尺寸依赖上转换发光
通常情况下,纳米颗粒尺度越大,表面所占比例越小;若在其中掺杂 Yb/Er 稀土离子后,可观察到随着颗粒尺度增大,其上转换红 / 绿光发射比降低。这主要是由于 Er 离子红光发射能级受表面影响较大的原因。 最近,我们在 CaF 2 -LnF 3 (Ln=Yb, Lu) 无序固溶体纳米晶中掺杂 Er 离子后发现,随着纳米晶 ...
个人分类: 科学研究|4234 次阅读|1 个评论 热度 1