Materials Characterization—谭小东、逯文君等—冷轧超快速退火Q&P钢的组织性能

已有 886 次阅读 2022-7-4 13:13 |个人分类:学术报告|系统分类:论文交流

image.png

Abstract:

We performed ultra-fast heating (150 °C/s) quenching and partitioning (Q&P) processes to a cold-rolled low-carbon low-alloy steel. Adjusting the annealing temperature, we obtained two types of ferrite-containing Q&P steels with different matrix structure, i.e., martensitic matrix and ferritic matrix. The effect of ultra-fast heating on microstructure evolution and mechanical properties was analyzed, compared with the samples treated with conventional heating rate (10 °C/s). We also investigated the strain partition and fracture behaviors, basing on in-situ tensile tests under SEM. Results show that ultra-fast heating can significantly increase the Ac1 and Ac3 temperatures, and extend the temperature span of intercritical zone. It can also delay the complete recrystallization of deformed ferrite and promote the austenite nucleation, which leads to the structure refinement of the sample with martensitic matrix, improving both the strength and ductility. The increase of austenite nucleation rate and the incomplete recrystallization of deformed ferrite jointly promote the austenite transformation, which results in a distinct increase of martensite islands fraction in the sample with ferritic matrix, leading to its obvious increase of tensile strength and decrease of ductility. Strain partition is an important factor affecting the TRIP effect in ferrite-containing Q&P steels. For the sample with a martensitic matrix, retained austenite mainly possesses a film-like morphology and exists between martensite laths. The relatively high mechanical stability of retained austenite films and low local strain in martensitic regions result in the weak TRIP effect. The retained austenite in the sample with a ferritic matrix mainly distributes among ferrite grains and exhibits a blocky morphology. The relatively low mechanical stability of blocky retained austenite and high local strain in ferrite jointly enhance the TRIP effect.

下载链接:https://www.sciencedirect.com/science/article/abs/pii/S1044580322003680



https://wap.sciencenet.cn/blog-3362821-1345798.html

上一篇:西南大学材料与能源学院—谭小东等在先进高强钢应变配分研究领域取得系列进展
收藏 IP: 183.227.234.*| 热度|

0

该博文允许注册用户评论 请点击登录 评论 (0 个评论)

数据加载中...

Archiver|手机版|科学网 ( 京ICP备07017567号-12 )

GMT+8, 2022-9-30 04:21

Powered by ScienceNet.cn

Copyright © 2007- 中国科学报社

返回顶部