高体积含量梯度组织镁合金组织特点、退火行为及力学性能

已有 2426 次阅读 2017-3-5 17:09 |系统分类:论文交流

Evolution of gradient microstructure in an extruded AZ31 rod during torsion and annealing and its effects on mechanical properties
http://dx.doi.org/10.1016/j.msea.2017.02.042
Abstract

In this study, the AZ31 rods with gradient distributions of stored dislocations, {10–12} twins and texture components are fabricated by the free-end-torsion processing firstly. Influences of annealing treatment on the gradient microstructures and mechanical properties are then investigated. The results show that the annealing does not vary the torsion-deformed textures, but may cause recovery and recrystallization motivated by releasing of the stored dislocations. And the recrystallization behavior closely depends on the shear strain. High shear strain can generate high stored energy and increase the thermal mobility of {10–12} twin boundaries, resulting in the reduction of recrystallization temperature and promotion of nucleation. After annealing, recrystallization grain size gradually decreased from center to edge positions. Prior to annealing, the gradient hardness distribution in torsion-deformed sample is mainly attributed to the gradient dislocations. After annealing, grain size becomes the dominated factor for the hardening. Torsion deformation can almost eliminate yield asymmetry without the loss of strength and plasticity. Remarkable low yield asymmetry can be ascribed to grain refinement by twins and the textural change. With increasing annealing temperature up to 300 °C, yield asymmetry increases continuously owing to the grain growth induced by the static recrystallization. Finally, the relevant mechanisms are investigated and discussed.


http://www.sciencedirect.com/science/article/pii/S0921509317302009




http://wap.sciencenet.cn/blog-58154-1037649.html

上一篇:A Composite Technique for Preconditioning of Gear Material
下一篇:材料的素化 vs 高熵化

0

该博文允许注册用户评论 请点击登录 评论 (0 个评论)

数据加载中...

Archiver|手机版|科学网 ( 京ICP备07017567号-12 )

GMT+8, 2021-5-15 01:44

Powered by ScienceNet.cn

Copyright © 2007- 中国科学报社

返回顶部