The Y-doped MgZnCa alloys with ultrahigh specific strength

已有 4076 次阅读 2012-5-7 00:34 |个人分类:非晶前沿|系统分类:论文交流| Strength, specific

The Y-doped MgZnCa alloys with ultrahigh specific strength and good corrosion resistance in simulate body fluid

J.F. Wang^a^,^b^,

Y.Y. Wei^a^,^b,

S.F. Guo^c^,

S. Huang^a^,^b,

X.E. Zhou^a^,^b,

F.S. Pan^a

^a National Engineering Research Center for Magnesium Alloys, Chongqing University, Chongqing 400044, PR China
^b College of Materials Science and Engineering, Chongqing University, Chongqing 400044, PR China
^c School of Materials Science and Engineering, Southwest University, Chongqing 400715, PR China

Abstract
The microalloying effects of Y on the microstructure, mechanical properties and bio-corrosion resistances of Mg₆₉Zn₂₇Ca₄ (at.%) alloy were investigated by X-ray diffraction, compressive tests and electrochemical treatments, respectively. The Y-bearing Mg-Zn-Ca alloys were found to possess an ultrahigh compressive strength above 1000 MPa as well as high specific strength of 3.44 × 10⁵ N m kg^- 1. The enhanced mechanical properties can be attributed to the ductile dendrite phase, Mg₁₂YZn, which is dispersed in the matrix with the Y addition. Furthermore, the Y-doped Mg-Zn-Ca alloys studied in this work have much better corrosion resistance than traditional ZK60 and pure Mg alloys in simulated body fluid (SBF) at 37 °C, which could be good candidates to be used as biomedical materials

http://dx.doi.org/10.1016/j.matlet.2012.04.130

http://www.sciencedirect.com/science/article/pii/S0167577X12006222?v=s5

转载本文请联系原作者获取授权，同时请注明本文来自郭胜锋科学网博客。
链接地址：https://wap.sciencenet.cn/blog-4773-567941.html

上一篇：【本科毕设】导师为学生做毕设？
下一篇：Bioactive calcium titanate coatings on a Zr-based BMG

收藏 IP: 123.144.2.*| 热度|

数据加载中...

返回顶部

博文发布时间已经超过87600小时，评论已关闭。

扫一扫，分享此博文