Abstract: The room temperature compressive plasticity of Fe75Mo5P10C8.3B1.7 bulk metallic glass (BMG) was improved from 0.5% to 1.8% by increasing the sample diameter from 1.5 mm to 2.0 mm. With increasing the sample diameter to 2.0 mm, a heterogeneous microstructure with in-situ formed α-Fe dendrite sparsely distributed in the amorphous matrix can be attained. This heterogeneous microstructure is conceived to be highly responsible for the enhanced global plasticity in this marginal Fe-based BMG. |
Key words: bulk metallic glass; composite; rapid-solidification; mechanical property http://www.sciencedirect.com/science/article/pii/S1003632611611825 http://www.ysxbcn.com/Html_Article/En_16174.html |