我们采用水热方法合成了“花状”Ni3(NO3)2(OH)4 和 Zn5(OH)8(NO3)2(H2O)2 化合物，并以此为模板得到了具有纳米多孔结构的NiO和ZnO材料，并研究了其光学性能。相关研究结果发表在CrystEngComm 13, 1831 (2011)上
论文全文：
(a,b,c) FE-SEM images of the synthesized Ni3(NO3)2(OH)4 flowers; (d) typical TEM image of the individual flower, (e) HR-TEM image of a flake of flowers, and (f) SAED pattern of Ni3(NO3)2(OH)4 flower.
(a, b) FE-SEM image of microflower synthesized at 150 °C and 0.1M Zn(NO3)2·6H2O in 1 h;
(a) FE-SEM image of NiO flower (obtained from heating Ni3(NO3)2(OH)4 flowers in air at 400 °C for 3 h); (b) typical TEM image of the individual NiO flower; (c) magnified TEM image of the petal and (d)HR-TEM image of a flake of NiO flowers; (e) SAED pattern of NiO flowers.
(a, b) FESEM images of ZnO obtained after heating zinc compound in air at 400 oC for 3 h; (c) typical TEM image of a ZnO flake; (d) HRTEM image of a flake of a ZnO microflower and the inset is the SAED pattern of as-synthesized ZnO.
https://wap.sciencenet.cn/blog-39459-432750.html
上一篇：Fe 注入BaTiO3薄膜的磁性、铁电及磁电耦合性能
下一篇：台湾之行
扫一扫，分享此博文
全部作者的精选博文
- • 我的物理，我的大学（75）
- • 又到基金评审时
- • 我的物理，我的大学（68）
- • 我的物理，我的大学（66）
- • 我的物理，我的大学（63）
- • 扶上马，送一程