BoSonga ZhiwenDua NingGuoa QingshanYangb FangWanga ShengfengGuoa RenlongXinc
Abstrct
In this study, a rolled AZ31 bar with square section was used. The reciprocating torsion was performed to maintain the shape of the sample. The microstructure evolution of AZ31 bar during torsion and its influence on compressive anisotropy were investigated in detail. Results showed that reciprocating torsion can simultaneously enhance yield strength in three compressive directions, and reduce compressive anisotropy. Reciprocating torsion generated profuse dislocations and {102} twin boundaries to harden the micro-hardness and yield strength. Reciprocating torsion can also generate new texture component which is mainly from the orientation of newly generated {102} twins. The new twin-structures will be responsible for the reduction in compressive anisotropy. Moreover, uneven deformation features in twisted sample were systematically investigated.
https://www.sciencedirect.com/science/article/pii/S100503022030712X
转载本文请联系原作者获取授权,同时请注明本文来自郭胜锋科学网博客。
链接地址:https://wap.sciencenet.cn/blog-4773-1246750.html?mobile=1
收藏